Coloured soda-lime glass

ABSTRACT

The present invention relates to a coloured soda-lime glass which comprises iron in a quantity which, expressed in weight of the oxide Fe 2 O 3  in relation to the total weight of glass, is greater than or equal to 0.5, and less than or equal to 1.0% (quantity of total iron), a ratio of Fe 2+ /total Fe (redox ratio) in the range of between 20 and 65%, cerium in a quantity which, expressed in weight of CeO 2  in relation to the total weight of glass, is greater than or equal to 0.1%, and titanium in a quantity which, expressed in weight of TiO 2  in relation to the total weight of glass, is greater than or equal to 0% and less than 0.2%. This glass has a light transmission (TLA4) in the range of between 15 and 55%, a total transmission in the ultraviolet (TUV4) of less than or equal to 30%, and a dominant wavelength in transmission (λ D ) of less than or equal to 491 nm. This glass can be used, for example, as side glazing, rear-view window, roof glazing or opening roof of a motor vehicle.

The present invention relates to a coloured soda-lime.

Soda-lime glass can be dear or coloured, for example, green, grey or blue in transmission.

The expression “soda-lime glass” is used here in the wide sense and relates to any glass which is likely to contain the following principal glass-forming constituents (in percentages by weight): SiO₂ 60 to 75% Na₂O 10 to 20% CaO 0 to 16% K₂O 0 to 10% MgO 0 to 10% Al₂O₃ 0 to 5% BaO 0 to 2% BaO + CaO + MgO 10 to 20% K₂O + Na₂O 10 to 20%. B₂O₃ 0 to 5%

In some cases, soda-lime glass can have a total percentage by weight of BaO, CaO and MgO greater than 10%, and even greater than 12%.

This type of glass is very widely used in the field of glazing for automobiles or buildings, for example. It is usually manufactured in the form of a ribbon by the float process. Such a ribbon can be cut into sheets which can then be bent or can undergo treatment to improve their mechanical properties, e.g. a thermal toughening step.

It is generally necessary to relate the optical properties of a glass sheet to a standard illuminant. In the present description, two standard illuminants are used: illuminant C and illuminant A defined by the Commission Internationale de l'Eclairage (C.I.E.). Illuminant C represents average daylight having a colour temperature of 6700 K. This illuminant is especially useful for evaluating the optical properties of glazing intended for buildings. Illuminant A represents the radiation of a Planck radiator with a temperature of about 2856 K This illuminant describes the light emitted by car headlights and is essentially intended to evaluate the optical properties of glazings intended for automobiles.

The Commission Internationale de l'Eclairage has also published a document entitled “Colorimétrie, Recommandations Officielles de la C.I.E. [Colorimetry and Official Recommendations of the CIE]” (May 1970) which describes a theory in which the colorimetric coordinates for light of each wavelength of the visible spectrum are defined so that they can be represented on a diagram having orthogonal axes x and y, called the C.I.E. trichromaticity plot 1931. This trichromaticity plot shows the locus representative of light of each wavelength (expressed in nanometers) of the visible spectrum. This locus is called the “spectrum locus” and light having coordinates lying on this spectrum locus is said to have 100% excitation purity for the appropriate wavelength. The spectrum locus is closed by a line called the purple boundary which connects the points of the spectrum locus, the coordinates of which correspond to wavelengths of 380 nm (violet) and 780 nm (red). The area lying between the spectrum locus and the purple boundary is that available for the trichromaticity coordinates of any visible light. The coordinates of the light emitted by illuminant C, for example, correspond to x=0.3101 and y=0.3162. This point C is regarded as representing white light, and consequently has an excitation purity equal to zero for any wavelength. Lines may be drawn from point C to the spectrum locus at any desired wavelength and any point lying on these lines may be defined not only by its x and y coordinates, but also as a function of the wavelength corresponding to the line on which it lies and of its distance from point C relative to the total length of the wavelength line. Consequently, the colour of the light transmitted by a coloured glass sheet may be described by its dominant wavelength (λD) and its excitation purity (P) expressed as a percentage.

The C.I.E. coordinates of light transmitted by a coloured glass sheet will depend not only on the composition of the glass but also on its thickness. In the present description, as in the claims, all the values of the excitation purity P and the dominant wavelength λ_(D) of the transmitted light are calculated from the spectral specific internal transmissions (SIT_(λ)) of a glass sheet 5 mm in thickness with illuminant C from a solid viewing angle of 2°. The spectral specific internal transmission of a glass sheet is governed solely by the absorption of the glass and can be expressed by the Beer-Lambert law: SIT _(λ) =e ^(−E.A) ^(λ)

where A_(λ) is the absorption coefficient (in cm⁻¹) of the glass at the wavelength in question and E the thickness (in cm) of the glass. In a first approximation, SIT_(λ) may also be represented by the formula: (I₃+R₂)/(I₁−R₁) where I₁ is the intensity of the incident visible light on a first face of the glass sheet, R₁ is the intensity of the visible light reflected by this face, I₃ is the intensity of the visible light transmitted from the second face of the glass sheet and R₂ is the intensity of the visible light reflected by this second face towards the interior of the sheet.

The following are also used in the following description and the claims:

-   -   for illuminant A, the total light transmission (TLA) measured         for a thickness of 4 mm (TLA4) from a solid viewing angle of 2°.         This total transmission is the result of the integration between         the 380 and 780 nm wavelengths of the expression: Σ         T_(λ).E_(λ).S_(λ)/Σ E_(λ).S_(λ) in which T_(λ) is the         transmission at wavelength λ, E_(λ) is the spectral distribution         of illuminant A and S_(λ) is the sensitivity of the normal human         eye as a function of wavelength λ;     -   the total energy transmission (TE) measured for a thickness of 4         mm (TE4). This total transmission is the result of the         integration between the 300 and 2500 nm wavelengths of the         expression: Σ T_(λ).E_(λ)/Σ E_(λ). The energy distribution E_(λ)         is the spectral energy distribution of the sun at 30° above the         horizon with an air mass equal to 2 and an inclination of the         glazing of 60° relative to the horizontal. This distribution,         called “Moon distribution”, is defined in the standard ISO 9050;     -   the selectivity (SE) measured as the ratio of the total light         transmission for illuminant A to the total energy transmission         (TLA/TE);     -   the total transmission in the ultraviolet, measured for a         thickness of 4 mm (TUV4). This total transmission is the result         of the integration between 280 and 380 nm of the expression: Σ         T_(λ).U_(λ)/Σ U_(λ) in which U_(λ) is the spectral distribution         of the ultraviolet radiation that has passed through the         atmosphere, defined in the standard DIN 67507;     -   the Fe²⁺/total Fe ratio, sometimes called the redox ratio, which         represents the value of the ratio of weight of atoms of Fe⁺² to         the total weight of iron atoms present in the glass and is         obtained by the formula:         Fe ²⁺/total Fe=[24.4495×log(92/τ₁₀₅₀)]/t _(−Fe2O3)

where τ₁₀₅₀ represents the specific internal transmission of the 5 mm thick glass at the 1050 nm wavelength, t_(−Fe2O3) represents the total iron content expressed in the form of oxide Fe₂O₃ and measured by X-ray fluorescence.

Coloured glass can be used in architectural applications and as glazing for railway carriages and motor vehicles. In architectural applications, glass sheets 4 to 6 mm in thickness are generally used, while in the automotive field thicknesses of 1 to 5 mm are normally employed, particularly for the production of monolithic glazing, and thicknesses of between 1 and 3 mm in the case of laminated glazing, especially for windscreens, two glass sheets of this thickness then being bonded together by means of an interlayer film, generally made of polyvinyl butyral (PVB).

One of the objects of the invention is to provide a soda-lime glass of low light transmission, preferably blue in colour, which enables the unpleasing discolouration of the objects located inside areas enclosed by this glass to be restricted.

The European patent application EP 0 101 36 20 A1 and the international application PCT/EP01/06861 describe highly selective glasses containing iron with a high redox ratio (Fe²⁺/total iron), and also cobalt and/or chromium and/or vanadium respectively. However, to promote a high redox ratio may be detrimental to other optical properties such as total transmission in the ultraviolet which is responsible for the discolouration of objects located inside areas enclosed by such glasses.

The invention proposes glass compositions which have all the desired properties and in particular that of a filter for ultraviolet solar radiation.

The present invention provides a coloured soda-lime glass which comprises the principal glass-forming constituents and colouring agents comprising:

-   -   iron in a quantity which, expressed in weight of the oxide Fe₂O₃         in relation to the total weight of glass, is greater than or         equal to 0.5, and less than or equal to 1.0% (quantity of total         iron),     -   ferrous iron in a quantity which, expressed in weight of atoms         of Fe²⁺ in relation to the total weight of iron atoms present in         the glass, lies in the range of between 20 and 65% (ratio of         Fe²⁺/total Fe),     -   cerium in a quantity which, expressed in weight of CeO₂ in         relation to the total weight of glass, is greater than or equal         to 0.1%,     -   titanium in a quantity which, expressed in weight of TiO₂ in         relation to the total weight of glass, is greater than or equal         to 0% and less than 0.2%,

and the glass has:

-   -   a light transmission, measured for illuminant A and calculated         for a thickness of 4 mm (TLA4), which lies in the range of         between 15 and 55%,     -   a total transmission in the ultraviolet measured for a thickness         of 4 mm (TUV4) of less than or equal to 30%,     -   a dominant wavelength in transmission (λ_(D)) of less than or         equal to 491 nm.

It has been found that such a glass allows commercially desirable considerations relating to both aesthetics and energy to be met. In the automotive sector in particular a coloured glass according to the invention can have a blue tint, with a wavelength in transmission of less than or equal to 491 nm, which is appreciated by motor vehicle manufacturers, a low light transmission and a low total transmission in the ultraviolet enabling the unpleasing discolouration of the objects located inside areas enclosed by this glass to be restricted.

The presence of cerium in a quantity which, expressed in weight of CeO₂ in relation to the total weight of glass is greater than or equal to 0.1%, combined with the composition criteria relating to iron, allows a glass to be produced with a wavelength in transmission, light transmission and total transmission in the ultraviolet that meet present criteria relating to aesthetics and energy, especially required by motor vehicle manufacturers.

Iron is present in the majority of glasses currently on the market, in particular in coloured glasses. The presence of Fe³⁺ provides the glass with a light absorption of the visible light of short wavelength (410 and 440 nm) and a very high absorption band in the ultraviolet (absorption band centred at 380 nm), while the presence of Fe²⁺ ions causes a high absorption in the infrared (absorption band centred at 1050 nm). The presence of Fe³⁺ gives the glass a slight yellow coloration, generally regarded as not very pleasing, while ferrous, Fe²⁺, ions give a pronounced blue-green coloration. A strong concentration of Fe²⁺ in the glass therefore allows the energy transmission TE to be reduced and a pleasing coloration to be provided. However, the presence of iron in the bath of molten glass results in an absorption of infrared radiation which can hinder heat diffusion in the glass production furnace, and therefore make this production more difficult. Moreover, when the concentration of iron increases, the light transmission of the glass decreases.

The energy and optical properties of a glass, in particular its colour, its light transmission and its total transmission in the ultraviolet, result from a complex interaction between its components. The behaviour of components of the glass depends on their redox state and therefore on the presence of other components which can influence this redox state.

It has been found that the glass as defined in the claims enables aesthetic criteria (colour) and optical/energy criteria (light transmission and total transmission in the ultraviolet) to be responded to by easily controlling its composition, particularly in terms of iron and cerium.

Preferably, the quantity of total iron is less than or equal to 0.90%, and preferably less than or equal to 0.89%. This facilitates the transition of the production of clear glass to the production of coloured glass.

Preferably, the quantity of total iron is at least 0.7% or even at least 0.75%. This promotes not only the formation of a colour that is pleasing to the eye, but also the formation of a low light transmission as well as a low energy transmission.

Preferably, the glass according to the invention comprises ferrous iron in a quantity which, expressed in weight of atoms of Fe²⁺ in relation to the total weight of iron atoms present in the glass, lies in the range of between 20 and 65%, preferably between 35 and 55%, and advantageously between 40 and 50%. Such a ratio enables a glass to be obtained that combines a good selectivity with a low transmission in the ultraviolet.

Preferably, the glass according to the invention comprises cerium in a quantity which, expressed in weight of CeO₂ in relation to the total weight of glass, is greater than 0.15%, preferably greater than 0.25%, in order to restrict as far as possible the unpleasing discoloration of objects located inside areas enclosed by the glass according to the invention under the effect of ultraviolet solar radiation. The glass according to the invention preferably comprises cerium in a quantity which, expressed in weight of CeO₂ in relation to the total weight of glass, is less than 1.0%, preferably less than or equal to 0.5%. In fact, cerium, when present in too large a quantity, can cause the dominant wavelength to shift towards green and yellow, which is contrary to the preferred tint.

The invention advantageously combines a high redox ratio with a quantity of cerium which enables the desired properties to be provided without the aesthetic aspect of the glass being impaired.

Preferably, the glass according to the invention comprises a quantity of titanium which, expressed in weight of TiO₂ in relation to the total weight of glass, is greater than or equal to 0% and less than 0.2%, and preferably less than 0.15%, or even less than 0.10%. In fact, a high content of TiO₂ poses the risk of imparting an unwanted yellow coloration. In some cases, TiO₂ will only be contained in the glass as a result of the presence of impurities, with no intentional addition.

To produce a glass with a colour which is commercially desirable as it is considered to be pleasing to the eye, the glass according to the invention can contain one or more of the following colouring agents in addition to those already mentioned.

-   -   cobalt

The presence of cobalt tends to give the glass an intense blue colour. Preferably, the glass according to the invention comprises cobalt in a quantity which, expressed in weight of Co in relation to the total weight of glass, is greater than 75 ppm, and even greater than 100 ppm. Preferably, the quantity of cobalt is less than or equal to 350 ppm, and advantageously less than or equal to 250 ppm. A quantity of cobalt that is too high can in fact impair the selectivity of the glass.

In a preferred form, the glass according to the invention comprises the principal glass-forming constituents and colouring agents, the colouring agents consisting essentially of Fe, Ce and Co according to at least one of the ranges mentioned above. Ti may possibly be added to this composition.

In another preferred form, the glass according to the invention comprises the principal glass-forming constituents and colouring agents, the colouring agents consisting of Fe, Ce and Co according to at least one of the ranges mentioned above. Ti may possibly be added to this composition.

-   -   chromium

The presence of Cr^(III) tends to give the glass a light green coloration, whereas the presence of Cr^(VI) produces a very intense absorption band of 365 nm and a yellow coloration of the glass. Preferably, the glass comprises chromium in a quantity which, expressed in weight of Cr₂O₃ in relation to the total weight of glass, is at least 5 parts per million (ppm). In some cases, the glass can comprise chromium in a quantity that is greater than or equal to 50 ppm, and even greater than or equal to 100 ppm. Preferably the quantity of chromium is less than 1000 ppm, and advantageously less than or equal to 500 ppm.

In a preferred form, the glass according to the invention comprises the principal glass-forming constituents and colouring agents, the colouring agents consisting essentially of Fe, Ce, Co and Cr according to at least one of the ranges mentioned above. Ti may possibly be added to this composition.

In another preferred form, the glass according to the invention comprises the principal glass-forming constituents and colouring agents, the colouring agents consisting of Fe, Ce, Co and Cr according to at least one of the ranges mentioned above. Ti may possibly be added to this composition.

-   -   vanadium

The presence of vanadium tends to give the glass a green tint. Preferably, the glass according to the invention comprises vanadium in a quantity which, expressed in weight of V₂O₅ in relation to the total weight of glass, is less than 1000 ppm, and advantageously less than 500 ppm. In some cases, V₂O₅ will only be contained in the glass as a result of the presence of impurities, with no intentional addition.

The light transmission TLA4 of the coloured glass according to the invention lies in the range of between 15 and 55%, preferably between 20 and 45%, and advantageously between 25 and 35%. This makes this glass well suited for use, for example, as glazing for motor vehicles, in particular for side glazing, rear-view windows, roof glazing or also opening roofs.

The total transmission in the ultraviolet (TUV4) of the coloured glass according to the invention is preferably less than or equal to 30%, but can be less than or equal to 25%, and advantageously less than or equal to 20%. Such values for TUV4 help to prevent the unpleasing discoloration of objects located in areas enclosed by such a glass and exposed to ultraviolet solar radiation.

It is desirable if the coloured glass according to the invention has an energy transmission TE4 of less than 45%, preferably less than 35%, and advantageously less than 25%. A low energy transmission helps limit the temperature increase in the internal area enclosed by the glass according to the invention, such as a building or motor vehicle, during exposure to the sun.

The glass according to the invention preferably has a selectivity greater than 1.0, preferably greater than 1.1. A high selectivity is advantageous both for applications in motor vehicles and in architectural applications, since it helps limit the temperature increase associated with solar radiation, and thus increase the thermal comfort of occupants of the vehicle or building while providing high natural illumination and visibility through the glazing.

With respect to the colour of the glass according to the invention, it is desirable if its dominant wavelength in transmission λ_(D) is less than or equal to 489 nm. This corresponds to a glass whose colour in transmission is generally tinted blue, which is pleasing to the human eye and is highly appreciated commercially, in particular for glazing for motor vehicles. It is advantageous if the glass has a λ_(D) of less than or equal to 487 nm.

The excitation purity in transmission of the glass according to the invention is preferably greater than 10%, and preferably greater than 15%. This corresponds to a pronounced tint, which is commercially desirable. In some cases, the excitation purity in transmission can be greater than or equal to 20%, and even greater than 25%.

In some cases, the glass according to the invention can comprise less than 200 parts per million (ppm), preferably less than 100 ppm, of nickel, expressed in weight of NiO in relation to the total weight of glass. The presence of nickel can impair the selectivity of the glass containing it, since it does not absorb light in the infrared range, which results in a significant energy transmission value. In addition, it gives the glass a yellow coloration. Moreover, the presence of nickel can cause difficulties in the production of glass (formation of sulphides, inclusions of nickel in the glass). In particular embodiments, the glass according to the invention is free of nickel as colouring agent.

Preferably, the glass according to the invention comprises less than 1500 parts per million, preferably less than 500 parts per million, of manganese expressed in weight of MnO₂ in relation to the total weight of glass. Manganese in the form of MnO₂ has an oxidising character which can modify the redox state of the iron and induce a green hue.

Preferably, the glass according to the invention comprises more than 2% by weight of magnesium oxide MgO in relation to the total weight of glass. The presence of magnesium benefits the fusion of the constituents during melting of the glass.

Advantageously, the glass according to the invention comprises less than 30 parts per million of selenium, preferably less than 20 parts per million by weight of Se in relation to the total weight of glass. The presence of selenium as colouring agent can promote a low light transmission, but if present in too large a quantity, it can give the glass an unwanted pink or red coloration.

According to a preferred form of the invention, the colouring agents are present in a quantity corresponding to the following proportions (expressed as a percentage of the total weight of glass in the form indicated): Fe₂O₃ 0.5-1.0% CeO₂ 0.1-0.95% Co 130-160 ppm Cr₂O₃ 150-950 ppm Se 0-10 ppm TiO₂ 0-0.15% Fe²⁺/total Fe 30-50%

This glass preferably has the following optical properties: TLA4 15-55% TE4 <45% TUV4 ≦30% λ_(D) ≦491 nm P >10% and ≦35%

According to a particularly preferred form of the invention, the colouring agents are present in a quantity corresponding to the following proportions (expressed as a percentage of the total weight of glass in the form indicated): Fe₂O₃ 0.7-0.9% CeO₂ 0.2-0.7% Co 135-150 ppm Cr₂O₃ 300-500 ppm Se 0-10 ppm TiO₂ 0-0.15% Fe²⁺/total Fe 35-45%

This glass preferably has the following optical properties: TLA4 25-40% TE4 20-30% TUV4 10-20% λ_(D) 480-490 nm P 20-35%

According to a preferred embodiment, the glass according to the invention comprises the principal glass-forming constituents and colouring agents, the colouring agents consisting essentially of Fe, Ce, Co, Cr and Se according to at least one of the ranges mentioned above. Ti may possibly be added to this composition.

In another preferred form, the glass according to the invention comprises the principal glass-forming constituents and colouring agents, the colouring agents consisting of Fe, Ce, Co, Cr and Se according to least one of the ranges mentioned above. Ti may possibly be added to this composition.

It is desirable if the glass according to the invention does not contain fluorinated compounds, or at least if these do not constitute more than 0.2% by weight of F in relation to the glass. These compounds in fact generate furnace discharges which are harmful to the environment and are, moreover, corrosive with respect to the refractory materials which line the inside of the production furnace.

The coloured glass according to the invention preferably forms a glazing for motor vehicles. It may, for example, be advantageously used for side glazing or rear-view windows of a vehicle or roof glazing or opening roofs.

The glass according to the invention may be coated with a layer. For example, this can be a layer of metal oxides, which reduce the temperature increase resulting from solar radiation and consequently the temperature increase inside the passenger compartment of a vehicle using such glass as glazing.

The glasses according to the invention can be manufactured by conventional processes. As batch materials, it is possible to use natural materials, recycled glass, slag or a combination of these materials. The colouring agents are not necessarily added in the form indicated, but this manner of giving the amounts of colouring agents added in equivalents in the forms indicated corresponds to standard practice. In practice, iron is added in the form of red iron oxide, cobalt is added in the form of hydrated sulphate, such as CoSO₄.7H₂O or CoSO₄.6H₂O and chromium is added in the form of dichromate such as K₂Cr₂O₇. Cerium is often introduced in oxide or carbonate form, and vanadium in the form of vanadium oxide or sodium vanadate. Selenium, when present, can be added in elemental form or in selenite form such as Na₂SeO₃ or ZnSeO₃.

Other elements are sometimes present as a result of impurities in the batch materials used to manufacture the glass according to the invention, whether these are natural materials, recycled glass or slag, which are increasingly used, but when these impurities do not give the glass properties outside the limits defined above, these glasses are regarded as complying with the present invention.

The present invention shall now be illustrated by the following examples:

EXAMPLES 1 to 143

Table I specifies by way of non-restrictive indication the base composition of the glass. It should be understood that a glass with the same optical and energy properties can be obtained with a base composition having amounts of oxides lying within the ranges of percentages by weight given at the beginning of the present description.

The glasses according to the examples comprise less than 100 parts per million (ppm) of NiO, less than 500 ppm of MnO₂ and, unless specified otherwise, less than 3 ppm of Se, less than 0.1% of TiO₂ and more than 2% of MgO. TABLE I Analysis of the base glass SiO₂ 71.5-71.9% Al₂O₃ 0.8% CaO 8.8% MgO 4.2% Na₂O 14.1%  K₂O 0.1% SO₃ 0.05-0.45%

The following table gives the concentrations of the components, the optical and energy properties of glasses according to the invention. The concentrations are determined by X-ray fluorescence of the glass and are converted to the indicated molecular state. TABLE II Fe²⁺/ Fe₂O₃ Fe tot CeO₂ Co Cr₂O₃ Se TLA4 TUV4 λ_(D) TE4 P Ex. (%) (%) (%) (ppm) (%) (ppm) (%) (%) (nm) (%) (%) SE 1 0.875 32.73 0.29 150 351 32.9 12.6 483.3 25.9 30.2 1.27 2 0.873 35.42 0.49 146 352 33.0 11.8 483.4 24.9 30.2 1.32 3 0.893 41.52 0.10 152 352 31.4 15.8 482.9 22.4 33.3 1.40 4 0.874 33.58 0.49 147 354 32.8 11.2 483.5 25.5 29.8 1.29 5 0.871 33.28 0.39 145 355 32.7 11.7 483.6 25.7 29.7 1.27 6 0.870 32.72 0.49 147 362 32.7 11.1 483.6 25.8 29.6 1.27 7 0.848 24.12 0.97 142 359 34.9 8.3 484.4 31.4 25.3 1.11 8 0.890 39.35 0.10 152 343 31.7 16.0 482.8 23.1 33.0 1.37 9 0.867 35.19 0.48 146 352 32.4 11.7 483.4 24.8 30.5 1.31 10 0.873 39.08 0.29 141 347 32.4 13.8 483.3 23.5 31.3 1.38 11 0.850 25.65 0.97 138 363 35.2 8.3 484.8 30.5 24.8 1.15 12 0.854 48.24 0.29 143 298 29.6 14.3 482.4 20.4 35.8 1.45 13 0.854 46.99 0.285 148 308 31.8 14.1 483.2 21.5 32.9 1.48 14 0.861 47.85 0.28 168 310 29.7 14.4 482.5 20.6 35.4 1.44 15 0.898 49.89 0.30 148 354 29.9 12.9 483.4 19.6 33.8 1.53 16 0.900 50.25 0.30 155 362 29.3 13.4 482.5 19.3 36.1 1.52 17 0.882 45.50 0.30 149 322 29.3 13.3 482.0 20.6 36.1 1.42 18 0.908 48.94 0.32 151 329 28.6 13.1 482.5 19.1 36.5 1.50 19 0.906 49.05 0.30 160 333 27.5 12.9 482.1 18.7 37.8 1.47 20 0.906 48.24 0.30 164 333 28.5 12.7 482.5 19.3 36.3 1.48 21 0.864 30.81 0.68 145 313 33.8 10.1 483.2 27.4 29.1 1.23 22 0.852 24.58 0.89 144 310 34.9 8.6 483.6 31.3 26.6 1.15 23 0.850 23.97 0.97 141 316 35.3 8.3 483.8 31.9 25.8 1.11 24 0.847 43.34 0.30 139 341 30.5 14.2 482.3 22.2 34.9 1.37 25 0.800 44.00 0.30 140 400 30.3 15.4 482.6 22.6 34.6 1.34 26 0.750 45.00 0.30 145 450 29.5 16.8 482.7 22.7 35.3 1.30 27 0.700 45.00 0.50 145 500 29.7 15.6 483.0 23.9 34.7 1.24 28 0.650 47.00 0.50 150 500 28.9 16.9 482.5 23.5 36.5 1.22 29 0.700 45.00 0.40 155 400 28.8 16.7 481.6 23.7 38.0 1.22 30 0.600 45.00 0.70 160 380 29.5 15.4 480.8 26.4 39.4 1.12 31 0.550 45.00 0.70 155 550 29.8 16.9 482.4 27.0 36.2 1.10 32 0.700 45.00 0.50 150 450 29.3 15.6 482.3 23.8 36.3 1.23 33 0.500 50.00 0.90 155 590 28.2 15.8 482.6 25.0 37.6 1.13 34 0.600 40.00 0.90 150 50 35.7 12.2 478.0 32.4 38.7 1.10 35 0.850 40.00 0.90 140 50 33.4 6.3 479.6 26.4 36.3 1.26 36 0.600 50.00 0.90 150 0 32.1 12.1 478.0 26.1 43.0 1.23 37 0.850 40.00 0.90 140 0 33.8 6.1 479.1 26.7 37.0 1.26 38 0.875 50.00 0.90 100 50 36.1 5.4 481.7 21.8 32.1 1.66 39 0.850 55.00 0.90 70 50 39.8 5.7 483.1 21.1 28.3 1.88 40 0.875 60.00 0.90 50 300 39.0 5.5 487.7 17.0 23.2 2.29 41 0.850 50.00 0.90 30 0 49.2 5.3 485.5 27.2 19.6 1.81 42 0.847 40.00 0.30 139 340 31.8 14.2 482.3 24.4 33.7 1.30 43 0.850 44.00 0.30 140 500 28.8 14.5 483.9 20.8 33.2 1.39 44 0.850 45.00 0.30 150 200 29.9 13.8 483.9 21.5 33.2 1.39 45 0.850 45.00 0.30 170 100 28.9 13.6 479.3 21.5 44.3 1.34 46 0.850 40.00 0.30 190 50 29.5 13.5 478.3 24.5 46.9 1.20 47 0.850 45.00 0.30 200 0 27.0 13.4 478.0 21.2 51.2 1.28 48 0.850 45.00 0.30 250 380 19.6 14.2 480.1 17.5 54.9 1.12 49 0.600 25.00 0.95 350 20 24.9 11.4 475.4 36.8 69.9 0.68 50 0.875 45.00 0.90 76 600 32.4 6.9 489.8 21.3 19.8 1.52 51 0.850 50.00 0.11 105 600 29.0 17.0 486.2 17.1 28.4 1.69 52 0.850 50.00 0.90 120 500 27.8 7.3 485.1 17.9 30.3 1.55 53 0.700 55.00 0.90 160 0 28.6 9.7 478.6 20.3 46.2 1.41 54 0.850 30.00 0.90 165 500 31.6 7.2 483.5 29.7 31.1 1.07 55 0.850 45.00 0.90 180 380 25.3 7.0 481.9 20.1 40.8 1.26 56 1.000 40.00 0.30 139 340 29.3 10.6 482.9 20.4 33.4 1.44 57 0.950 44.00 0.30 140 500 27.2 12.1 484.3 18.1 39.1 1.50 58 0.970 45.00 0.30 150 200 28.0 11.0 481.1 18.4 39.1 1.52 59 1.000 45.00 0.30 170 100 17.6 10.1 479.9 17.6 44.0 1.51 60 1.000 40.00 0.30 190 50 27.1 10.0 479.0 20.5 46.6 1.32 61 0.970 45.00 0.30 200 0 25.1 10.6 478.5 18.0 50.9 1.39 62 0.850 45.00 0.10 160 380 27.8 16.6 481.9 16.6 39.2 1.39 63 0.850 45.00 0.10 140 550 28.2 17.0 484.2 20.0 33.4 1.44 64 0.850 45.00 0.95 140 700 26.3 7.1 486.5 19.5 29.5 1.35 65 0.900 40.00 0.95 140 800 26.7 6.1 488.2 20.9 26.5 1.28 66 0.875 45.00 0.90 150 950 23.1 7.7 488.8 23.1 17.0 1.35 67 0.900 40.00 0.50 237 600 20.0 11.1 482.1 18.7 47.2 1.07 68 0.700 35.00 0.90 5 30 50.0 9.7 485.3 37.8 10.7 1.32 69 0.700 30.00 0.20 34 30 50.0 18.1 481.1 39.7 15.8 1.26 70 0.510 55.00 0.10 165 500 28.0 24.9 481.6 21.6 42.7 1.29 71 0.850 45.00 0.90 280 380 16.4 7.0 479.9 17.1 58.9 0.96 72 0.970 45.00 0.90 200 600 19.9 4.7 483.6 15.1 41.3 1.32 73 0.990 45.00 0.90 220 600 17.8 4.2 483.1 13.9 44.9 1.27 74 0.850 30.00 0.20 48 455 42.9 15.6 490.9 32.8 12.9 1.31 75 0.850 20.00 0.90 200 380 33.4 6.94 481.0 35.8 35.4 0.93 76 0.850 25.00 0.20 180 380 33.8 15.4 481.1 32.6 35.4 1.04 77 0.850 20.00 0.30 180 380 35.6 14.1 481.1 35.9 33.3 0.99 78 0.850 50.00 0.20 140 300 28.1 15.3 481.9 17.9 38.2 1.57 79 0.850 50.00 0.40 150 380 26.5 15.3 482.4 17.3 38.5 1.53 80 0.820 30.00 0.40 100 380 39.2 13.7 482.4 32.7 38.5 1.20 81 0.800 33.00 0.40 80 200 41.6 13.8 482.4 32.9 38.5 1.27 82 0.750 35.00 0.40 50 180 44.4 14.9 482.4 33.9 38.5 1.31 83 0.850 32.00 0.20 40 150 45.3 14.9 482.4 33.5 38.5 1.35 84 0.650 40.00 0.20 20 50 48.0 19.4 482.4 34.7 38.5 1.38 85 0.800 32.00 0.40 15 20 49.2 13.4 482.4 36.5 38.5 1.35 86 0.847 43.34 0.30 139 341 30.5 14.2 482.3 22.2 34.9 1.37 87 0.850 44.00 0.30 140 340 10 27.8 14.1 482.8 20.3 28.3 1.37 88 0.900 45.00 0.30 145 450 30 20.3 13.2 487.6 14.8 14.4 1.38 89 0.850 45.00 0.50 175 500 30 15.3 12.4 485.0 14.0 18.9 1.09 90 1.000 50.00 0.50 190 500 15.0 9.0 482.4 9.8 44.1 1.53 91 1.000 50.00 0.40 156 400 30 15.1 9.7 485.8 8.5 18.4 1.77 92 0.850 45.00 0.70 145 300 20 24.2 9.3 483.2 18.6 22.2 1.30 93 0.900 45.00 0.50 130 0 20 28.6 9.7 479.6 19.8 23.8 1.44 94 0.890 40.00 0.70 100 0 30 33.6 7.3 483.3 24.1 8.8 1.39 95 0.880 50.00 0.90 120 35 25 27.0 5.4 481.6 17.2 18.7 1.57 96 0.900 40.00 0.90 130 0 28 28.4 4.9 479.9 22.4 15.4 1.27 97 0.847 43.34 0.30 139 341 30.5 14.2 482.3 22.2 34.9 1.37 98 0.850 44.00 0.30 140 340 4 29.1 14.1 482.4 21.1 32.5 1.38 99 0.900 45.00 0.20 145 450 7 25.6 14.4 483.8 17.7 30.5 1.44 100 0.850 45.00 0.50 163 500 15 20.8 12.3 484.0 16.8 27.0 1.24 101 1.000 50.00 0.50 180 400 3 16.9 8.7 482.1 10.6 41.4 1.59 102 1.000 50.00 0.40 156 400 6 20.5 9.7 483.2 11.7 35.0 1.75 103 0.850 45.00 0.70 145 300 14 25.6 9.3 482.7 19.4 26.4 1.32 104 0.900 45.00 0.50 130 0 13 30.2 9.7 479.6 20.7 28.7 1.46 105 0.890 40.00 0.90 100 0 15 36.8 4.9 481.7 26.2 18.7 1.40 106 0.880 50.00 0.80 100 550 11 29.7 7.6 489.8 17.2 18.7 1.72 107 0.900 40.00 0.30 130 500 15 27.9 13.2 486.9 20.7 19.5 1.35 108 0.900 40.00 0.30 130 450 15 28.3 13.1 486.1 21.0 20.1 1.35 109 0.900 40.00 0.30 130 400 15 28.7 13.0 485.3 21.3 20.7 1.35 110 0.900 42.00 0.30 130 350 15 28.3 12.9 484.4 20.2 22.0 1.40 111 0.950 45.00 0.40 130 500 27.6 10.9 484.8 17.9 31.4 1.55 112 0.850 44.00 0.40 110 500 31.4 13.3 485.3 21.7 27.6 1.45 113 0.850 50.00 0.40 120 450 28.6 13.2 484.2 17.8 32.2 1.60 114 0.800 50.00 0.30 100 500 30.8 15.7 485.3 19.3 28.3 1.59 115 0.825 40.00 0.80 100 550 33.6 9.1 487.1 25.4 22.9 1.32 116 0.800 45.00 1.00 160 300 28.5 6.8 481.6 22.6 38.1 1.26 117 0.850 45.00 1.00 140 380 28.8 5.8 483.2 21.4 33.4 1.35 118 0.850 45.00 1.00 125 370 30.2 5.8 483.7 21.9 30.8 1.38 119 0.850 45.00 0.95 115 400 30.9 6.4 484.4 22.0 28.8 1.41 120 0.855 25.00 0.95 110 450 38.7 6.4 486.1 34.8 20.1 1.11 121 0.875 45.00 0.50 115 450 30.5 11.4 484.7 20.6 29.2 1.48 122 0.950 50.00 0.40 105 490 28.0 10.9 485.7 15.4 28.9 1.82 123 0.850 59.00 0.40 120 500 24.6 13.3 484.5 11.6 34.8 2.12 124 0.700 64.00 0.40 80 400 29.5 16.6 484.4 14.1 30.9 2.09 125 0.850 65.00 0.50 75 400 27.0 11.9 485.4 9.7 30.0 2.78 126 0.850 60.00 0.40 80 380 28.8 13.1 485.0 12.9 29.6 2.24 127 0.850 42.00 0.30 120 500 31.4 14.5 484.8 22.7 28.9 1.39 128 0.850 43.00 0.30 130 600 29.3 14.7 485.4 21.1 29.8 1.39 129 0.855 40.00 0.30 140 650 29.1 14.7 485.6 22.4 29.9 1.30 130 0.825 45.00 0.30 115 500 31.1 15.1 484.8 21.5 29.1 1.44 131 0.800 45.00 0.30 105 490 32.4 15.6 485.1 22.5 27.5 1.44 132 0.850 45.00 1.00 100 0 35.4 4.9 480.4 35.4 31.2 1.43 133 0.830 45.00 1.35 120 300 31.3 1.9 483.4 23.3 30.0 1.34 134 0.810 47.00 0.10 105 460 31.9 17.7 484.5 21.0 29.1 1.52 135 0.828 41.92 0.29 148 379 31.8 15.3 483.0 23.1 32.8 1.38 136 0.800 40.00 0.90 105 100 37.0 7.5 480.9 28.5 29.3 1.30 137 0.850 45.00 0.30 185 850 21.7 15.2 485.4 16.7 37.1 1.29 138 0.850 46.00 0.30 180 800 22.1 15.1 485.1 16.5 37.2 1.34 139 0.850 45.00 0.80 175 750 22.9 9.0 485.3 18.0 35.4 1.27 140 0.875 47.00 0.10 175 750 22.3 16.9 484.8 15.5 37.8 1.44 141 0.845 35.00 0.80 200 700 25.1 9.0 484.0 24.2 36.9 1.04 142 0.856 40.00 0.30 187 750 24.0 12.5 484.7 20.5 36.4 1.16 143 0.845 35.00 0.80 115 200 36.6 7.9 481.9 29.7 28.2 1.23 

1-36. (canceled)
 37. Coloured soda-lime glass which comprises principal glass-forming constituents and colouring agents: total iron in a quantity which, expressed in weight of the oxide Fe₂O₃ in relation to the total weight of glass, is greater than or equal to 0.5% and less than or equal to 1.0%; ferrous iron in a quantity which, expressed in weight of atoms of Fe²⁺ in relation to total weight of iron atoms present in the glass (ratio of Fe²⁺/total Fe), lies in the range of between 20% and 65%; cerium in a quantity which, expressed in weight of CeO₂ in relation to the total weight of glass, is greater than or equal to 0.1%; titanium in a quantity which, expressed in weight of TiO₂ in relation to the total weight of glass, is greater than or equal to 0% and less than 0.2%; and the glass has: a light transmission, measured for illuminant A and calculated for a thickness of 4 mm (TLA4), which lies in the range of between 15% and 55%; a total transmission in the ultraviolet measured for a thickness of 4 mm (TUV4) of less than or equal to 30%; and a dominant wavelength in transmission (λ_(D)) of less than or equal to 491 nm.
 38. Coloured soda-lime glass according to claim 37, characterised by at least one of the following (A) through (I): (A) the quantity of total iron is further defined as being: (i) less than or equal to 0.90%; (ii) less than or equal to 0.89%; (iii) at least 0.70%; (iv) at least 0.75%; (v) (i) and (iii); or (vi) (ii) and (iv); (B) the quantity of cerium is further defined as being: (i) greater than 0.10%; (ii) greater than 0.15%; (iii) less than or equal to 0.50%; or (iv) (ii) and (iii); (C) the quantity of titanium is further defined as being: (i) less than 0.15%; or (ii) less than 0.10%; (D) cobalt is present as a colouring agent in a quantity which, expressed in weight of Co in relation to the total weight of glass, is: (i) greater than 75 ppm; (ii) greater than 100 ppm; (iii) less than or equal to 350 ppm; (iv) less than or equal to 250 ppm; (v) (i) and (iv); or (vi) (ii) and (iii); (E) chromium is present as a colouring agent in a quantity which, expressed in weight of Cr₂O₃ in relation to the total weight of glass, is: (i) at least 5 ppm; (ii) at least 50 ppm; (iii) at least 100 ppm; (iv) less than 1000 ppm; (v) less than 500 ppm; (vi) less than or equal to 500 ppm; or (vii) (iii) and (v); (F) the quantity of Fe²⁺ is further defined being: (i) within the range of between 35% and 55%; or (ii) within the range of between 40% and 50%; (G) TLA4 is further defined as being: (i) within the range of between 20% and 45%; or (ii) within the range of between 25% and 35%; (H) TUV4 is further defined as being: (i) less than or equal to 25%; or (ii) less than or equal to 20%; (I) λ_(D) is further defined as being: (i) less than or equal to 489 nm, or (ii) less than or equal to 487 nm.
 39. Coloured soda-lime glass according to claim 38, further characterised by at least two of the aforementioned features (A) through (I).
 40. Coloured soda-lime glass according to claim 38, further characterised by at least three of the aforementioned features (A) through (I).
 41. Coloured soda-lime glass according to claim 38, further characterised by at least four of the aforementioned features (A) through (I).
 42. Coloured soda-lime glass according to claim 38, further characterised by all of the aforementioned features (A) through (I).
 43. Coloured soda-lime glass according to claim 38, characterised by at least one of the following (J) through (N): (J) vanadium is present as a colouring agent in a quantity which, expressed in weight of V₂O₅ in relation to the total weight of glass, is: (i) less than 1000 ppm; or (ii) less than 500 ppm; (K) selenium is present as a colouring agent in a quantity which, expressed in weight of Se in relation to the total weight of glass, is: (i) less than 30 ppm; or (ii) less than 20 ppm; (L) the glass has an energy transmission measured according to the Moon distribution and calculated for a thickness of 4 mm (TE4) of: (i) less than 45%; (ii) less than 35%; or (iii) less than 25%; (M) the glass has a selectivity (SE4) which is: (i) greater than 1.0; or (ii) greater than 1.1; (N) the glass has an excitation purity in transmission which is: (i) greater then 10% or (ii) greater than 15%.
 44. Coloured soda-lime glass according to claim 43, further characterised by at least two of the aforementioned features (J) through (N).
 45. Coloured soda-lime glass according to claim 43, further characterised by at least three of the aforementioned features (J) through (N).
 46. Coloured soda-lime glass according to claim 43, further characterised by all of the aforementioned features (J) through (N).
 47. Coloured soda-lime glass according to claim 37, characterised by at least one of the following (J) through (N): (J) vanadium is present as a colouring agent in a quantity which, expressed in weight of V₂O₅ in relation to the total weight of glass, is: (i) less than 1000 ppm; or (ii) less than 500 ppm; (K) selenium is present as a colouring agent in a quantity which, expressed in weight of Se in relation to the total weight of glass, is: (i) less than 30 ppm; or (ii) less than 20 ppm; (L) the glass has an energy transmission measured according to the Moon distribution and calculated for a thickness of 4 mm (TE4) of: (i) less than 45%; (ii) less than 35%; or (iii) less than 25%; (M) the glass has a selectivity (SE4) which is: (i) greater than 1.0; or (ii) greater than 1.1; (N) the glass has an excitation purity in transmission which is: (i) greater then 10% or (ii) greater than 15%.
 48. Coloured soda-lime glass according to claim 47, further characterised by at least two of the aforementioned features (J) through (N).
 49. Coloured soda-lime glass according to claim 47, further characterised by at least three of the aforementioned features (J) through (N).
 50. Coloured soda-lime glass according to claim 47, further characterised by all of the aforementioned features (J) through (N).
 51. Coloured soda-lime glass according to claim 38, further characterised in that the colouring agents consist essentially of iron, cerium, titanium and cobalt.
 52. Coloured soda-lime glass according to claim 38, further characterised in that the colouring agents consist of iron, cerium, titanium and cobalt.
 53. Coloured soda-lime glass according to claim 38, further characterised in that the colouring agents consist essentially of iron, cerium, titanium, cobalt and chromium.
 54. Coloured soda-lime glass according to claim 38, further characterised in that the colouring agents consist of iron, cerium, titanium, cobalt and chromium.
 55. Coloured soda-lime glass according to claim 37, characterised in that it is covered by a layer. 